PVDF Granules Injection Moulding Mfr 6-26 PVDF Pellet Resin

• CAS No.: 24937-79-9
• Formula: -(CH2-CF2)N-
• EINECS: 24937-79-9
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: pvdf granule
• Molecular Principal Chain: Homopolymer
• Color: White
• Density: 1.77-1.79g/cm3
• Melting Point: 165~170
• Tensile Breaking Strength: >25MPa
• Elongation at Break: >20%
• Mfr: 6-26
• Transport Package: Packaged in Polythene Bags
• Specification: 25kg/pkg
• Trademark: FeiTengYa
• Origin: China
• HS Code: 3904690000
• Production Capacity: 15000 Tons Per Year

Product Description

1. Product Description
Polyvinylidene fluoride resin is a polyvinylidene fluoride polymer prepared by emulsion process. Its high purity, with excellent chemical corrosion resistance, oxidation resistance, radiation resistance and good mechanical properties, suitable for architecture grade film application and to be molded into pipe fittings, pumps and valves and other parts of various specifications.

2. Product Index

No.	Properties	Unit	Typical value	Test method
1	Appearance	-	White particle	Visual inspection
2	Solubility(DMAC)	-	Clear and transparent, not cloudy, solution without impurities	T-FSI 027-2019
3	Density	g/cm3	1.77-1.79	GB/T 1033.1
4	Water content	Wt%	≤0.10	HG/T 2902
5	Durometer hardness	Shore D	74~80	ASTM D2240, GB/T 2411
6	MFR@230ºC5kg	g/10min	6~26	ASTM D1238
7	Tensile breaking strength	Mpa	≥25	ASTM D638, GB/T1040.1 50mm/min@23ºC
8	Elongation at break	%	≥20	ASTM D638, GB/T1040.1 50mm/min@23ºC
9	Tensile Strength, Yield	Mpa	≥25	ASTM D638, GB/T1040.1 50mm/min@23ºC
10	Elongation at Yield	%	≥10	ASTM D638, GB/T1040.1 50mm/min@23ºC
11	Melting Point	ºC	165~170	GB/T 19466.4
12	Thermal decomposition temperature	ºC	370	TGA

 

Applications